Condensation-crosslinking two-component dental molding material made of alkoxysilyl-and hydroxysilyl-functional polyethers

ABSTRACT

Condensation-crosslinking two-component dental molding materials based on polyethers, which are particularly suitable for taking impressions, as well as mixtures that can be obtained from them, and their use. Such materials are used in dental medicine, for example for taking tooth impressions, for bite registration, or for lining dental prostheses. The material contains the following: at least one alkoxysilyl-functional polyether a),  
     at least one reinforcing filler b 1 ) having a BET surface of at least 50 m 2 /g or at least one non-reinforcing filler b 2 ) having a BET surface of less than 50 m 2 /g, water c), if applicable, at least one condensation catalyst d), and a hydroxylsilyl-functional polyether e).

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to condensation-crosslinking two-component dental molding materials based on polyethers, which are particularly suitable for taking impressions, as well as mixtures that can be obtained from them, and their use. Such materials are used in dental medicine, for example for taking tooth impressions, for bite registration, or for lining dental prostheses.

2. The Prior Art

Condensation-crosslinking dental molding materials usually contain hydroxyl-functional polymers with a silicon backbone, which crosslink and cure in the presence of water and metallorganic catalysts, for example organic tin or titanium compounds. However, such materials are comparatively hydrophobic, because of the silicon backbone of the polymers, so that significant proportions of surfactant must be added to them, for the purpose of reducing the surface tension and to adjust the required wettability.

As an alternative to this, two-component dental molding materials are known that Contain polymers having terminal alkoxysilyl groups and a hydrophilic polyether backbone, which demonstrate sufficiently hydrophilic properties for wetting of the moist tooth substance. Usually, these materials consist of a base component containing alkoxysilyl-functional polyether having an average molecular weight of 800 to 20,000 g/mol, which can also have urea and/or urethane groups, as a function of their synthesis, fillers, as well as any other necessary additives, and a catalyst component that contains not only fillers and any other necessary additives but also an organic and/or inorganic acid as the catalyst.

Condensation-crosslinking two-component dental molding materials are described in European Patent No. EP 0 269 819 B1, the base component of which contains polyaddition products containing alkoxysilyl end groups, having a predominantly linear molecular structure and an average molecular weight of 800 to 20,000 g/mol, which have a content of polyether groups of 25 to 90 wt.-%, a content of urethane groups of 0.5 to 10 wt.-%, a content of urea groups of 0.5 to 10 wt.-%, as well as a content of terminal alkoxysilyl groups of 1 to 25 wt.-%, and the catalyst component of which contains a mixture containing water as well as organic and/or inorganic acids in weight amount ratios (water/acid) of 1:0.01 to 1:40.

European Patent No. EP 1 226 808 A2 discloses condensation-crosslinking two-component dental molding materials consisting of a base component and a catalyst component, the base component of which contains alkoxysilyl-functional polyethers having a linear or branched main chain and an average molecular weight of 800 to 20,000 g/mol, which have a content of polyether groups of 20 to 95 wt.-%, a content of terminal alkoxysilyl groups of 0.2 to 25 wt.-%, as well as a content of urethane groups or urea groups of up to 10 wt.-%, if necessary, and the catalyst component of which contains a mixture containing water as well as organic and/or inorganic acids in weight amount ratios of 1:0.01 to 1:40. Preferably, the catalyst component contains p-toluene sulfonic acid hydrate as the catalyst, as well as a polyether diol and additional additives, such as fillers, paraffin, emulsifier, and the like.

However, the known dental materials based on alkoxysilyl ethers have the disadvantage of binding with insufficient rapidity. Furthermore, the catalyst mixture, which according to the state of the art must necessarily contain an acid, is limited with regard to the chemical nature and the amount of fillers that can be added, so that special additives, such as emulsifiers and/or thickeners, must be added to it, so that the two components can be mixed using mixer systems that are usual on the market. Because of the lack of flexibility with regard to the addition of fillers, the components of the dental material must furthermore be specially formulated in order to obtain components to be mixed in a ratio of 1:1.

SUMMARY OF THE INVENTION

It is therefore an object of the present invention to provide a hydrophilic condensation-crosslinking two-component dental molding material based on alkoxysilyl polyethers, which demonstrates faster binding kinetics as compared with those previously known, is flexible with regard to the chemical nature and amount of fillers to be added to the catalyst component, and furthermore can easily be formulated in the form of 1:1 systems.

According to the invention, this task is accomplished by means of a condensation-crosslinking two-component dental molding material containing at least one alkoxysilyl-functional polyether a), one reinforcing filler b₁) having a BET surface of at least 50 m²/g and/or at least one non-reinforcing filler b₂) having a BET surface of less than 50 m²/g, water c), if applicable, at least one condensation catalyst d), and a hydroxylsilyl-functional polyether e).

Surprisingly, it was found, within the scope of the present invention, that condensation-crosslinking two-component dental molding materials that contain hydroxylsilyl-functional polyethers e) in addition to alkoxysilyl-functional polyethers a) bind more quickly than materials comprising only alkoxysilyl-functional polyethers. Furthermore, it was found that the two-component dental materials according to the invention, containing both alkoxysilyl-functional and hydroxylsilyl-functional polyethers a), e) can be crosslinked and cured not only with acids, as described in the state of the art for dental materials that exclusively contain alkoxysilyl-functional polyethers, but also with other condensation catalysts, such as bases and metallorganic compounds, with reaction kinetics that are suitable for dental materials. Therefore the systems according to the invention are also more flexible than the materials previously known, with regard to the chemical nature and the amount of the fillers to be added to the catalyst component.

Fundamentally, all the polyethers containing hydroxylsilyl groups that are known to a person skilled in the art can be used as hydroxylsilyl-functional polyethers e), whereby the polyether backbone can be linear and/or branched, and can be composed, for example, of polyethylene oxide, polypropylene oxide, polytetrahydrofuran and/or their copolymers. These monomers can be present statistically, in blocks, or in a tactical arrangement. Monovalent or multivalent alcohols can be used as starters for the polyethers and/or copolymers, such as, for example, methanol, butanol, glycerin, trimethyl propane, pentaerythrite, and sorbitol. For example, copolymers of polytetrahydrofuran with polyethylene oxide or of polyethylene oxide and polypropylene oxide can be used, and pure polypropylene oxide is particularly preferred. Furthermore, polyethers having side-position alkyl groups are preferred, with every or at least every tenth monomer structural unit carried a side-position alkyl group.

Preferably, the hydroxylsilyl-functional polyethers e) have a numerically average molecular weight from 200 to 250,000 g/mol, particularly preferably from 400 to 100,000 g/mol, and very particularly preferably from 1,000 to 20,000 g/mol.

According to a preferred embodiment of the present invention, the hydroxylsilyl structural unit(s) of the at least one polyether e) is/are disposed exclusively terminally, with reference to the polymer backbone, and fall under the general formula SiR¹R²R³, where R¹, R² and R³, independent of one another, are hydrogen, alkyl, or hydroxy, with at least one radical being a hydroxyl group. Particularly preferably, the at least one polyether e) has a hydroxyl group content of 0.08 to 7.0 mmol/g, particularly preferably of 0.1 to 5, and very preferably of 0.1 to 1.0 mmol/g.

Preferably, the at least one hydroxylsilyl-functional polyether e) has a content of polyether groups between 1 and 30 mmol/g and particularly preferably between 2 and 25 mmol/g.

In another embodiment of the invention, the material contains polyethers e) that have alkylene spacers disposed on the preferably terminal hydroxylsilyl groups, in each instance, as the third structural unit, which spacers particularly preferably have C₁-C₆ alkyl groups, very particularly preferably C₁-C₃ alkyl groups, and most highly particularly preferably methylene groups.

Furthermore, the at least one polyether e) can have 0 to 8 mmol/g, particularly preferably 0 to 4 mmol/g, and very particularly preferably 0.02 to 2 mmol/g urethane groups and/or 0 to 8 mmol/g and particularly preferably 0 to 2 mmol/g urea groups as the fourth structural unit, as a function of the synthesis.

For example, the individual structural units of the at least one polyether e) can be disposed according to one of the following general formulas (I) and (II):

where x=1 to 6, preferably x=2 to 4, and very particularly preferably x=2, n=1 to 6, preferably n=1 to 3, and very particularly preferably n=1, as well as m=0 or 1, particularly preferably m=1, and R¹, R², R³, independent of one another, are hydrogen, alkyl, or hydroxyl, with at least one radical being a hydroxyl group, preferably R¹ and R³, independent of one another, are alkyl, as well as R²=hydroxyl and particularly preferably, R¹ and R³=methyl as well as R²=hydroxyl,

-   -   and/or         where x=1 to 6, preferably x=2 to 4, and very particularly         preferably x=2,         n=1 to 6, preferably n=1 to 3, and very particularly preferably         n=1, as well as l=0 or 1, particularly preferably l=1, and         R¹, R², R³, independent of one another, are hydrogen, alkyl, or         hydroxyl, with at least one radical being a hydroxyl group,         preferably R¹ and R³, independent of one another, are alkyl, as         well as R²=hydroxyl and particularly preferably, R¹ and         R³=methyl as well as R²=hydroxyl.

The production of these hydroxylsilyl-functional polyethers is known and is described, for example, in W. Ziche, “Isocyanatomethyl-dimethylmonomethoxysilane—A Building Block for RTV-2 Systems,” 2^(nd) European Organosilicon Days, Programs & Abstracts, which is hereby incorporated by reference.

Particularly good results are obtained, however, if the at least one hydroxylsilyl-functional polyether e) is a linear polyether, whereby linear polyethers having the general formula (III):

wherein A=NH or O,

-   -   R¹, R² independent of one another, are alkyl, aryl, aralkyl,         preferably methyl,     -   n is a whole number between 1 and 6, preferably between 1 and 3,         and particularly preferably 3,         [Polyether]=[CH₂—O]_(n1), [CH₂—CH₂—O]_(n2),         [CH₂—C(CH₃)H—O]_(n3),     -   [C(CH₃)H—CH₂—O]_(n4), [(CH₂—CH₂—CH₂—CH₂—O]_(n5) or     -   [CH₂—CRH—O]_(n6), where

-   R is alkyl, aryl, aralkyl,

-   n₁ is a whole number between 1 and 500, preferably between 1 and 10,

-   n₂ is a whole number between 1 and 1,000, preferably between 1 and     20,

-   n₃, n₄ independent of one another, are a whole number between 1 and     1,500, preferably between 1 and 300,

-   n₅ is a whole number between 1 and 100, preferably between 1 and 15,     and

-   n₆ is a whole number between 1 and 1500, preferably between 1 and     300,     are very particularly preferred.

According to a special embodiment of the present invention, the condensation-crosslinking two-component dental molding material contains at least one hydroxylsilyl-functional polyether e) according to the general formula (IV)

-   -   and/or the general formula (V)

Preferably, the two-component dental material according to the invention contains 10 to 80 wt.-%, particularly preferably 20 to 70 wt.-%, and very particularly preferably 30 to 70 wt.-% of at least one polyether e) that contains hydroxylsilyl groups, with reference to the total mixture.

According to a first embodiment of the present invention, the at least one catalyst d) is an acid, whereby organic or inorganic acids are preferred. In particular, sulfuric acid, phosphoric acid, dibutyl phosphoric acid, trifluoromethane sulfonic acid, tartaric acid, citric acid, adipinic acid, benzoic acid, 2-ethyl caproic acid or alkanic acid, and particularly preferably, p-toluene sulfonic acid have proven themselves to be particularly suitable, alone or in mixtures with one another.

Preferably, the catalyst component B of the total mixture, contains 0.01 to 2 wt.-%, particularly preferably 0.05 to 1.0 wt.-%, and very particularly preferably 0.05 to 0.5 wt.-% of at least one acid d).

According to a second embodiment of the present invention, the two-component dental molding materials according to the invention contain at least one base and/or one salt from a base with an acid as the catalyst d). With the exception of inorganic bases, such as alkali metal hydroxides, alkali metal carbonates, and the like, which are unsuitable for dental medicine applications because of their toxicological hazardousness and/or because of overly slow reaction kinetics, fundamentally all known bases, particularly organic bases, Lewis bases, basic ion exchanger resins, strong, sterically hindered bases and superbases are suitable for this purpose.

Particularly preferably, the two-component dental materials contain at least one strong, sterically hindered base as the catalyst d). Within the scope of the present invention, it was surprisingly found that when using strong, sterically hindered bases, in comparison with the use of other bases, only a very slight catalyst concentration is necessary in order to obtain dental material having suitable reaction kinetics, particularly a sufficiently long working and curing time. Because of the low amount of catalyst required, the resulting dental materials also demonstrate outstanding biocompatibility. Furthermore, in this manner, reaction kinetics with a snap effect, as described in European Patent No. EP 1 226 808 A2, which is herein incorporated by reference, are achieved. Furthermore, this catalyst system demonstrates good storage stability, and is neutral in terms of odor and taste, in contrast to dental impression materials using aziridinopolyethers, as they are disclosed, for example, in International Application No. PCT/EP02/05916, German Patent No. DE 197 53 456, and International Application No. PCT/EP01/13852.

Fundamentally, the two-component dental materials according to the invention can contain any of the strong, sterically hindered bases known to a person skilled in the art as the catalyst d), whereby

-   (CH₃)₂NC(═NH)N(CH₃)₂ 1, 1, 3, 3-tetramethylguanidine -   1,8-diazabicyclo[5.4.0]undec-7-ene (DBU), -   1,5-diazabicyclo[4.3.0]non-5-ene (DBN) -   tert-butylimino-tris(dimethylamino)phosphoran -   tert-butylimino-tri(pyrrolidino)phosphoran -   tert-octylimino-tris(dimethylamino)phosphoran -   2-tert-butylimino-2-diethylamino-1,3-dimethyl-perhydro-1,3,2-diazaphosphorine -   2-tert-butylimino-2-diethylamino-1,3-dimethyl-perhydro-1,3,2-diazaphosphorine     on polystyrene -   1-tert-butyl-2,2,4,4,4-pentakis(diethylamino)-2Λ5, 4Λ     5-catenadi(phosphazene) -   1-ethyl-2,2,4,4-pentakis(diethylamino)-2Λ5,     4Λ5-catenadi(phosphazene) -   1-tert-butyl-4,4,4-tris(dimethylamino)-2,2-bis[tris(dimethylamino)-phosphoranylidenamino]-2Λ⁵,     4Λ⁵-catenadi (phosphazene) -   1-tert-octyl-4,4,4-tris(dimethylamino)-2,2-bis[tris(dimethylamino)-phosphoranylidenamino]-2Λ⁵,     4Λ⁵-catenadi (phosphazene) -   2,8,9-triisobutyl-2,5,8,9-tetraaza-1-phosphabicyclo[3.3.3]undecane -   2,8,9-triisopropyl-2,5,8,9-tetraaza-1-phosphabicyclo[3.3.3]undecane -   2,8,9-trimethyl-2,5,8,9-tetraaza-1-phosphabicyclo[3.3.3]undecane     as well as 2-tert-butyl-1,1,3,3-tetramethylguanidine,     N,N-dicyclohexylmethylamine, N,N-diethylaniline,     N,N-diisopropyl-2-ethylbutylamine, N,N-diisopropylmethylamine,     N,N-diisopropyl-3-pentylamine, N,N-dimethylaniline,     2,6-di-tert-butyl-4-methylpyridine,     1,5,7-triazabicyclo(4.4.0)dec-5-ene,     7-methyl-1,5,7-triazabicyclo(4.4.0)dec-5-ene,     1,5-diazabicyclo(4.3.0)non-5-ene, 1,1,3,3-tetramethylguanidine,     quinuclidine, 2,2,6,6-tetramethylpiperidine, pempidine,     tributylamine, triethylamine, N-ethyldiisopropylamine,     3,3,6,9,9-pentamethyl-2,10-diazabicyclo-(4.4.0)dec-1-ene,     N,N,N′N′-tetramethyl-1,8-naphthalenediamine,     2,4,6-tri-tert-butylpyridine, and tris(trimethylsilyl)amine are     particularly preferred as strong, sterically hindered bases.     1,1,3,3-tetramethylguanidine, DBU, and DBN are particularly     preferred as the base catalyst.

All of the bases d) mentioned above can be used individually or in any desired combination with one another, in each instance. Preferably toxically compatible bases are used, which are sufficiently basic to demonstrate a sufficient catalytic effect even when used in small concentrations, and, if necessary, to achieve an additional effect, for example in connection with the desensitization of teeth.

In a further development of the idea of the invention, at least one salt from a base with an acid is used in place of or in addition to the at least one base as the catalyst d). Preferably, the at least one salt is either a salt from a strong, sterically hindered base with a weak acid, or a salt from a weak base with a strong acid. Particularly preferred examples of salts to be used according to the invention, produced from a strong base with a weak acid, are salt of diazabicycloundecane and/or 1,5-diazabicyclo[4.3.0]non-5-ene with alkanic acids, fatty acids, ethyl caproic acid, ascorbinic acid, salicylic acid, acetylsalicyclic acid, or benzoic acid. The acids last mentioned are preferably used for salt formation also because they demonstrate not only high catalysis activity but also medicinal substance properties, as well as a preservative and/or antioxidant effect. Particularly preferred examples of salts to be used according to the invention, from a strong acid with a weak base are salts of toluene sulfonic acid with pyridine or toluene sulfonic acid with N,N-2-,4-,6-pentamethylaniline. Aside from toluene sulfonic acid, sulfuric acid, fluorosulfonic acid, trifluoromethane sulfonic acid, or fluorosulfuric acid can also be used as strong acids, for example, whereas pyridine, pentamethylaniline, and pyrrol are other preferred examples of weak bases.

The use of at least one salt from a base with an acid is advantageous for several reasons. For one thing, a salt, in contrast to the use of a free base, or, as provided in the state of the art, a free acid, brings about a moderate pH. For the salt pair of a sterically hindered base with a weak acid, for example DBU with ethyl caproic acid, the pH preferably lies between 8 and 11, and particularly preferably between 8 and 9, whereas for the salt pair of a strong acid with a weak base, for example toluene sulfonic acid with pyridine, the pH is preferably between 2 and 7, and particularly preferably between 3 and 4. Because of these moderate pH values, good compatibility of the dental materials according to the invention with the mucous membranes of the mouth and with the tooth enamel is guaranteed, so that no etching or irritation will occur. Furthermore the moderate pH values of the stated catalyst salts, in other words the salts from a base with an acid, preferably of a strong base with a weak acid or of a strong acid with a weak base, impart an excellent storage stability to the dental materials, since these salts, in contrast to free acids or bases, are chemically inert with regard to the other ingredients of the dental material, in other words particularly do not enter into any secondary reactions or decomposition reactions with other ingredients, such as with fillers, for example, with the polyether used as a paste formation agent, or with the alkoxysilyl polyether, particularly during the storage period and after curing. In contrast to the stated catalyst salts d), strong bases, for example, attach the cristobalite that is frequently used as a filler in dental materials, or strong acids attack polyether and alkoxysilyl polyether, whereby the free base or the free acid, respectively, is used up and therefore the catalyst activity that was originally adjusted is reduced. This results in a longer curing time or in an extreme case actually prevents curing. A polymer decomposition as the result of secondary or decomposition reactions after curing would furthermore result in a lack of shape stability; such shape stability, however, is an absolute prerequisite for making a mold and producing a model.

Another advantage of the use of the catalyst salts d) provided according to the invention lies in the avoidance of interactions between the catalyst and active substance additives, since the pH can be directly adjusted to the requirements of the active substance by means of selecting a suitable catalyst salt, and therefore an unrestricted effectiveness of the active substances is guaranteed. Furthermore, the dental materials according to this embodiment demonstrate good biocompatibility, because of the surprisingly low concentrations of the stated catalyst salts that are required. Finally, the dental materials according to this embodiment are also characterized by excellent neutrality in terms of odor and taste, which is an important property for a dental molding material, in order to achieve patient acceptance and avoid gagging reactions of the patient during application, for example.

In the case of the first and second embodiment, in other words when using at least one acid, one base, or one salt from an acid and a base as the catalyst d), the alkoxysilyl-functional polyether a) is preferably contained in a component A of the two-component material, and the hydroxylsilyl-functional polyether e), water c), if water is provided, and the catalyst d) are contained in the component B, or both the alkoxysilyl-functional polyether a) and the hydroxylsilyl-functional polyether e) are contained in the component A, and the water c), if water is provided, as well as the catalyst d) are contained in the component B. If both the alkoxysilyl-functional polyether and the hydroxylsilyl-functional polyether are provided in the base component A, a water catcher should be added to this component, in order to prevent hydrolysis of the alkoxysilyl-functional polyether before the two components are mixed.

Preferably, the dental materials according to the invention contain 0.001 to 1 mmol/g, particularly preferably 0.001 to 0.5, and very particularly preferably 0.001 to 0.1 mmol/g of at least one base, which is preferably a strong, sterically hindered base, and/or 0.001 to 1.0 mmol/g, particularly preferably 0.001 to 0.5, and very particularly preferably 0.001 to 0.1 mmol/g of at least one salt from a strong base with a weak acid, and/or 0.0005 to 0.5 mmol/g, particularly preferably 0.0005 to 0.25, and very particularly preferably 0.0005 to 0.05 mmol/g of at least one salt from a weak base with a strong acid, in the catalyst component B, of the mixture.

The water c) that is optionally contained in the catalyst component B leads to the formation of silanol groups, by means of reaction with the alkoxy groups of the alkoxysilyl polyether, which groups in turn represent the reactive species for the condensation reaction. Preferably, the catalyst component B of the two-component dental molding material according to the invention contains 0.001 to 3%, particularly preferably 0.005 to 2%, and very particularly preferably 0.01 to 1.5% water c), with reference to the total mixture.

It has proven to be advantageous that the molar ratio of water to alkoxy groups, with reference to the total mixture, amounts to between 1:6 and 1:1.5, and particularly preferably between 1:4 and 1:2. Within the scope of the present invention, it has surprisingly been shown that reaction kinetics in keeping with dental requirements, in other words a comparatively long working time at a comparatively short dwell time in the mouth, with snap effect, is achieved if the water content of the total mixture is lower than the alkoxy group content of the total mixture.

According to a third embodiment of the present invention, the at least one catalyst d) is a metallorganic compound, preferably a metal alkoxide, a chelate and/or an oligocondensate or polycondensate of a metal alkoxide, a double metal alkoxide, in other words an alkoxide that contains two different metals in a specific ratio, a metal acylate, and/or a metal carboxylate. Examples of suitable metal alkoxides are those selected from among the group consisting of aluminum alkoxide, antimony alkoxide, barium alkoxide, boron alkoxide, calcium alkoxide, cerium alkoxide, erbium alkoxide, gallium alkoxide, silicon alkoxide, germanium alkoxide, hafnium alkoxide, indium alkoxide, iron alkoxide, lanthanium alkoxide, magnesium alkoxide, neodynium alkoxide, samarium alkoxide, strontium alkoxide, tantalum alkoxide, titanium alkoxide, tin alkoxide, vanadium alkoxide, yttrium alkoxide, zinc alkoxide, zirconium alkoxide and mixtures of them.

Particularly preferably, the at least one metallorganic compound is a titanium organic, zirconium organic, and tin organic compound, whereby titanium tetraethylate, titanium tetrapropylate, titanium tetraisopropylate, titanium tetrabutylate, titanium tetraisooctylate, titanium isopropylate tristeaorylate, titanium triisopropylate steaorylate, titanium diisopropylate disteaorylate, titanium triisopropylate-O-allyloxy(polyethylenylate), titanium allylacetoacetate triisopropylate, titanium bis(triethanolamine) diisopropylate, titanium chloride triisopropylate, titanium di-n-butylate (bis-2,4-pentane dionate), titanium dichloride diethylate, titanium diisopropylate bis-(2,4-pentane dionate), titanium diisopropylate bis(tetramethylheptane dionate), titanium tetraisobutylate, titanium dilactate, titanium methacrylate triisopropylate, zirconium tetrapropylate, zirconium tetraisopropylate, zirconium tetrabutylate, zirconium tetraethylate, zirconium hexafluoropentane dionate, zirconium dimethacrylate, zirconium trifluoropentane dionate, zirconium dimethacrylate dibutylate, tin dibutyl laurate, tin dibutyl mercaptide, tin dibutyl dicarboxylate, tin dioctyl dicarboxylate, tin bis(2-ethoxyhexaonate), tin bis(neodecanoate), tin tetraallylate, tin tetramethylate, tin tetravinylate, tin dimethyl hydroxyoleate, dialkyl tin diacetate, tin (II) octoate, dialkyl tin diacylate, dialkyl tin oxide are very particularly preferred.

In the case of this third embodiment, the hydroxylsilyl-functional polyether e) as well as the water c), if water is provided, are preferably contained in the component A, and the alkoxysilyl-functional polyether a) as well as the catalyst d) are contained in the component B, or both the alkoxysilyl-functional polyether a) and the hydroxylsilyl-functional polyether e) are contained in the component A, and the water c), if water is provided, as well as the catalyst d) are contained in the component B. In the case of the latter, a water catcher must necessarily be added to the base component A, in order to prevent hydrolysis of the alkoxysilyl-functional polyether before the two components are mixed.

Preferably, the catalyst component B contains 0.1 to 3.0%, particularly preferably 0.1 to 2.0%, and very particularly preferably 0.1 to 1.5% of at least one metallorganic compound as the catalyst d), with reference to the total mixture.

Fundamentally, all the polyethers containing alkoxysilyl groups can be used as alkoxysilyl-functional polyethers a), whereby the polyether backbone can be linear and/or branched, and can be composed, for example, of polyethylene oxide, polypropylene oxide, polytetrahydrofuran and/or their copolymers, whereby these monomers can be present statistically, in blocks, or in a tactical arrangement. Monovalent or multivalent alcohols can be used as starters for the polyethers and/or copolymers, such as, for example, methanol, butanol, glycerin, trimethyl propane, pentaerythrite, and sorbitol. For example, copolymers of polytetrahydrofuran with polyethylene oxide or of polyethylene oxide and polypropylene oxide can be used, whereby pure polypropylene oxide is particularly preferred. Furthermore, polyethers having side-position alkyl groups are preferred, whereby every or at least every tenth monomer structural unit carries a side-position alkyl group. Suitable commercial products are Acclaim® 6300, Acclaim® 2200, Acclaim® 8200, and Acclaim® 6300 from Bayer AG, Polyglycol P41/300 and Polyglycol P41/3000 (Clariant), as well as poly-(ethylenegylcol-ran-propyleneglycol) (Aldrich). Preferably, the polyethers have a numerically average molecular weight from 500 to 25,000 g/mol and particularly preferably from 5,000 to 20,000 g/mol.

According to a special embodiment of the present invention, the at least one alkoxysilyl-functional polyether a) has a content of polyether groups between 5 and 30 mmol/g and particularly preferably between 10 and 25 mmol/g.

Preferably, the alkoxysilyl structural unit(s) of the polyether a) is/are disposed terminally, with reference to the polymer backbone, and fall under the general formula SiR⁵R⁶R⁷, where R⁵, R⁶ and R⁷, independent of one another, are hydrogen, alkyl, or alkoxy. Particularly preferably, the at least one polyether has an alkoxy group content of 0.02 to 12 mmol/g, particularly preferably of 0.04 to 6, and very particularly preferably of 0.04 to 3 mmol/g.

The condensation kinetics and therefore the working and binding time of the dental molding material can be adjusted by means of the type and number of the alkoxy groups per silicon atom. Fundamentally, it holds true that alkoxy groups are all the more reactive, the shorter their alkyl groups are, so that methoxy groups are more reactive than ethoxy groups, and ethoxy groups in turn are more reactive than butoxy groups. Furthermore, the reaction kinetics of the condensation reaction increase with an increasing number of alkoxy groups per silicon atom, so that three methoxy groups bound per silicon atom are more reactive than two methoxy groups and one alkyl group per silicon atom. Both influences are correlated in such a manner that three silicon-bound ethoxy groups have approximately the same reactivity as one alkoxysilyl group with two methoxy groups and one alkyl group. Therefore the working and binding time can be adjusted to the desired value by means of the selection of the type and number of alkoxy groups per silicon atom, as well as by way of the type of alkylene spacer. Preferably, these parameters are selected in such a manner that the working time is 30 seconds to 3 minutes, particularly preferably between 1 and 2.5 minutes, and very particularly preferably between 1.5 and 2 minutes, and/or the binding time in the patient's mouth (so-called mouth dwell time) determined according to ISO 4823 is maximally 10 minutes, particularly preferably maximally 6 minutes, and very particularly preferably maximally 4 minutes.

Preferably, the at least one polyether a) has alkylene spacers disposed on the terminal alkoxysilyl groups, in each instance, as the third structural unit, which spacers particularly preferably have C₁-C₆ alkyl groups, very particularly preferably C₁-C₃ alkyl groups, and most highly particularly preferably methylene groups.

Furthermore, the at least one polyether a) can have 0 to 8 mmol/g, particularly preferably 0 to 4 mmol/g, and very particularly preferably 0.02 to 2 mmol/g urethane groups and/or 0 to 8 mmol/g and particularly preferably 0 to 2 mmol/g urea groups as the fourth structural unit, as a function of the synthesis. Particularly if the at least one polyether has a urea group and/or urethane group as the fourth structural unit, a methylene group is preferred as the spacer, because then the hydrolysis of the alkoxy groups proceeds particularly quickly, because of the slight spatial distance between the terminal alkoxysilyl group and the urethane group or urea group (so-called a effect). By means of the use of such α-activated alkoxysilyl polyethers, hydrophilic, storage-stable two-component dental molding masses are obtained, which crosslink surprisingly quickly, by means of a condensation reaction, with a basic catalyst and/or a catalyst salt from a strong base and a weak acid or from a strong acid and a weak base, according to the second embodiment of the present invention.

For example, the individual structural units of the at least one polyether a) can be disposed according to one of the following general formulas (VI) and (VII):

where x=1 to 6, preferably x=2 to 4, and very particularly preferably x=2, n=1 to 6, preferably n=1 to 3, and very particularly preferably n=1, as well as m=0 or 1, particularly preferably m=1, and R⁵, R⁶, R⁷ are as defined above, or

where x=1 to 6, preferably x=2 to 4, and very particularly preferably x=2, n=1 to 6, preferably n=1 to 3, and very particularly preferably n=1, as well as l=0 or 1, particularly preferably l=1, and R⁵, R⁶, R⁷ are as defined above.

The production of these alkoxysilyl-functional polyethers is known and is described, for example, in German Patent No. DE 101 04 079 A1, European Patent No. EP 0 629 819 B1, German Patent No. DE 101 39 132, U.S. Pat. No. 4,906,707, European Patent No. EP 0 372 561 A1, European Patent No. EP 1 303 560 A1, and European Patent No. EP 0 170 865 B1, which are hereby introduced as references and considered to be part of the disclosure. Examples of commercially available polyethers that are suitable within the scope of the present invention are MS Polymer™ S 203H, MS Polymer™ S 303H (Keneka), Polymer XP ST55, ST50, ST51, ST53 (Hanse), SLM 414000, SLM 414001 (Wacker), Baycoll® XP 2458, and Desmoseal® XP 2447 (Bayer AG).

According to a special embodiment of the present invention, the following alkoxysilyl-functional polyether a) is used: (CH₃O)₃—Si—(CH₂)₃—[O—CH₂—CH(CH₃)]_(n)—O—(CH₂)₃—Si(OCH₃)₃  Formula (VIII) where n=1 to 5,000, preferably n=1 to 300, and very particularly preferably n=1 to 80.

A particular advantage of this alkoxysilyl-functional polyether a) is that because of the absence of urethane and urea groups, it has only a very low viscosity, and is particularly stable with regard to water.

In the case of this embodiment, in which the at least one catalyst d) is necessarily a metallorganic compound, and the alkoxysilyl-functional polyether a) according to Formula (VIII) is used, the at least one alkoxysilyl-functional polyether a) as well as the water c), if water is provided, are preferably provided in the component A, whereas the at least one hydroxylsilyl-functional polyether e) and the catalyst d) are added to the catalyst component B.

Preferably, the two-component dental material according to the invention contains 10 to 80 wt.-%, particularly preferably 20 to 70 wt.-%, and very particularly preferably 30 to 70 wt.-% of at least one polyether a) that contains alkoxysilyl groups, with reference to the total mixture.

According to the invention, the component A of the dental molding material according to the invention contains at least one reinforcing filler b₁) and/or at least one non-reinforcing filler b₂), whereas the catalyst component B does not have to contain any filler. Preferably, however, the component B also contains at least one reinforcing filler b₁) and/or at least one non-reinforcing filler b₂).

Highly disperse, active fillers having a BET surface of at least 50 m²/g are particularly suitable as reinforcing fillers b₁) Those having an individual particle size in the nanometer range, which can be present as aggregates and/or agglomerates, are particularly suitable. Preferably, the at least one reinforcing filler b₁) is selected from the group that consists of aluminum hydroxide, zinc oxide, titanium oxide, zirconium oxide, silicon dioxide, as well as precipitated and/or pyrogenic silicic acid. Of course, the compounds mentioned above can be used individually or in any desired combination with one another, specifically also both in hydrophilic and in hydrophobized form.

Furthermore preferably, the at least one reinforcing filler b₁) is present in the form of nanoparticles, as a fiber-form or lamella-form filler, for example a mineral fiber-form filler, or as a synthetic fiber-form filler.

In a further development of the invention, it is proposed that the reinforcing filler b₁) provided in the component that contains the at least one alkoxysilyl-functional polyether a) has a water content of maximally 0.5 wt.-%, particularly preferably of maximally 0.3 wt.-%, and very particularly preferably of maximally 0.15 wt.-%, whereby the water content is determined by way of Karl Fischer titration, according to the invention.

According to a special embodiment of the present invention, the at least one reinforcing filler b₁) in the base component A has a pH between 5 and 9, and particularly preferably between 5.5 and 8.5. In this manner, degradation of the alkoxysilyl-functional polyethers during storage is avoided.

Preferably, the base component A of the dental molding material according to the invention contains 0 to 50 wt.-%, particularly preferably 0.1 to 40 wt.-%, and very particularly preferably 0.1 to 30 wt.-%, with reference to the component A, and the catalyst component B contains 0 to 50 wt.-%, particularly preferably 0.1 to 40 wt.-%, and very particularly preferably 0.1 to 30 wt.-% of at least one reinforcing filler b₁), with reference to the component B.

Fundamentally, the same substances as for the reinforcing fillers are suitable as non-reinforcing fillers b₂), whereby the non-reinforcing fillers necessarily have a BET surface of less than 50 m²/g (Schriftenreihe Pigmente Degussa Kieselsäuren/Degussa pigment monograph series, silicic acids/, No. 12, page 5, as well as No. 13, page 3). Preferably the at least one non-reinforcing filler is a substance selected from among the group that consists of earth alkali metal oxides, earth alkali metal hydroxides, earth alkali metal fluoride, earth alkali metal carbonates, calcium apatite (Ca₅[(F, Cl, OH, ½CO₃|(PO₄)₃], particularly calcium hydroxyl apatite (Ca₅[(OH)|(PO₄)₃], titanium dioxide, zirconium dioxide, aluminum hydroxide, silicon dioxide, precipitated silicic acid, and calcium carbonate. Of course, the compounds mentioned above can be used individually or in any desired combination with one another, specifically also both in hydrophilic and in hydrophobized form.

Preferably, the non-reinforcing fillers b₂) that are used have an average grain size greater than 0.1 μm (Ullmann's Encyclopädie der Technischen Chemie [Encyclopedia of technical chemistry], Volume 21, page 523).

In a further development of the invention, the non-reinforcing filler b₂) provided in the component that contains the at least one alkoxysilyl-functional polyether a) has a water content of maximally 0.5 wt.-%, particularly preferably maximally 0.1 wt.-%, and very particularly preferably maximally 0.05 wt.-%.

According to a special embodiment of the present invention, the at least one non-reinforcing filler b₂) in the base component A has a pH between 5 and 9, and particularly preferably between 5.5 and 8.5, in order to prevent degradation of the alkoxysilyl-functional polyethers during storage.

Preferably, the base component A of the dental molding material according to the invention contains 0 to 80 wt.-%, particularly preferably 0.05 to 75 wt.-%, and very particularly preferably 0.1 to 70 wt.-%, with reference to the component A, and the catalyst component B contains 0 to 80 wt.-%, particularly preferably 0.05 to 75 wt.-%, and very particularly preferably 0.1 to 70 wt.-% of at least one non-reinforcing filler c₂), with reference to the component B.

In total, the total content of fillers b₁), b₂) is preferably 0.01 to 80 wt.-%, particularly preferably 0.05 to 75 wt.-%, and very particularly preferably 0.1 to 70 wt.-%, with reference to the total mixture.

In a further development of the invention, it is proposed to add exclusively acid-stable ingredients to the dental materials according to the first embodiment of the present invention, in which at least one acid is used as the catalyst d), to add exclusively base-stable ingredients to the dental materials according to the second embodiment of the present invention, in which at least one base and/or at least one salt from strong bases and weak acids is used as the catalyst d), and to add exclusively acid-stable ingredients to the dental materials according to the second embodiment of the present invention, in which at least one salt from weak bases and strong acids is used as the catalyst d). Base-stable and acid-stable in the sense of the present invention refers to compounds that are so base-stable or acid-stable, even after a storage period of at least 12 months, that no noticeable deterioration of the reaction kinetics that were originally adjusted occurs.

According to another special embodiment of the present invention, the reinforcing and non-reinforcing fillers b₁), b₂) contained in the catalyst component B have a pH between 3.5 and 12. If free, strong, sterically hindered bases are used as the catalyst d), the catalyst component B preferably contains base-stable fillers b₁), b₂) having a pH between 6.0 and 12.0, and very particularly preferably those having a pH between 7.0 and 11.0. In the case of salts from strong, sterically hindered bases with weak acids as the catalyst, base-stable fillers having a pH between 6.0 and 11.0 are preferably used in the catalyst component B, and very particularly those having a pH between 7.0 and 10.0 are used. If salts from strong acids with weak bases are used as the catalyst d), the catalyst component B preferably contains base-stable fillers having a pH between 3.5 and 9.0, and very particularly preferably those having a pH between 5.0 and 8.5.

In a further development of the invention, one or more of the following additives and/or ancillary substances are added to the dental molding material according to the invention:

-   -   f) buffer salts,     -   g) water catchers,     -   h) paste forming agents,     -   i) surfactant,     -   j) active substance,     -   k) plasticizer,     -   l) substance allowing optical scanning,     -   m) flavor and/or fragrance,     -   n) substance allowing diagnosis,     -   o) fluoridation agent,     -   p) bleach substance,     -   q) desensitization agent,     -   r) adhesion bond imparting agent,     -   s) dye,     -   t) indicator,     -   u) stabilizer (antioxidant),     -   v) antibacterial substance.

Buffer salts f) can optionally be added, specifically preferably in the component containing the at least one alkoxysilyl-functional polyether a), to the dental molding material according to the invention, with which the pH of the catalyst component B and of the base component A can be adjusted. Buffer systems having a buffer salt selected from among the group consisting of alkali metal hydrogen carbonate, dialkali hydrogen phosphate, tris(hydroxymethyl)aminomethane, phthalic acid monoalkali salt, phthalic acid monotetramethyl ammonium salt, ammonium salts of amines, cyclic amines, amides, cyclic amides, and 4,4′-(oxidi-2,1-ethane-diyl)bismorpholine have proven themselves to be particularly suitable for this purpose. As a person skilled in the art will recognize, the addition of a buffer system f) is particularly practical for the first and second embodiment of the present invention, in which a free acid or a free base is used as the catalyst. Such an addition can, however, of course also be advantageous in the embodiment of the present invention in which a salt from a base with an acid is used as the catalyst, or in the third embodiment of the present invention, in which a metallorganic compound is used as the catalyst d).

According to another special embodiment of the present invention, the dental materials, specifically if the at least one alkoxysilyl-functional polyether a) and the at least one hydroxylsilyl-functional polyether e) are provided in the base component A, have at least one water catcher g), preferably in the base component A, which is particularly preferably selected from among the group that consists of alkoxysilanes, titanates, such as tetraisopropyltitanate, zirconates, such as tetrapropylzirconate, zeoliths, aluminum sulfate, anhydrous calcium sulfate (for example Drierite®), blue gel, and oxazolidines.

In a further development of the idea of the invention, it is proposed to use one or more functional alkoxysilanes as water catchers g), since the crosslinking speed, the structure, and the properties of the resulting elastomer can be adjusted by means of such compounds. Preferably, the at least one functional alkoxysilane is a compound having the general formula (IX) R⁸ _(4-x)—Si—R⁹ _(x)

-   -   where R⁸=H, alkyl, alkenyl, —(CH₂)_(n)—X, where n=1 to 6,         R⁹=alkoxy,     -   X=NH₂, NHR¹⁰, NR₂, whereby R¹⁰=alkyl, aminoalkyl, —CO, —OCH₃, as         well as X=0, 1, 2, 3, or 4,     -   whereby particularly preferably, R⁸=alkenyl or —(CH₂)_(n)—X with         X=NHR¹⁰ and n=1 or 3, and/or     -   x=3 or 4 and R¹⁰=—OCH₃.

Particularly preferably, the at least one functional alkoxysilane g) is vinyl trimethoxysilane and/or N-trimethoxysilylmethyl-O-methylcarbamate. The two compounds just mentioned are reactive silanes that not only increase the crosslinking speed during curing, but also function as water catchers g) for removing any traces of water that are still present in the component A of the dental composition, and thereby prevent a premature viscosity increase or crosslinking of the alkoxysilyl polyether during storage. Furthermore, by means of adding vinyl trimethoxysilane, which is installed into the elastomer network during the condensation reaction, the mechanical property of the cured dental material can be adjusted. In particular in the case of the dental molding materials according to the invention which have alkoxysilyl polyether a) with a methylene spacer at the terminal alkoxysilyl groups, it has proven to be advantageous to add both vinyl trimethoxysilane and N-trimethoxysilylmethyl-O-methylcarbamate to the component A, since here, the reactivity of vinyl trimethoxysilane alone is frequently not sufficient for stabilization with regard to water. Furthermore, N-trimethoxysilylmethyl-O-methylcarbamate in the component A leads to high cross-linking of the products resulting from the condensation reaction, after mixing with the catalyst component, and therefore results in cured dental materials having high tear strength, good elasticity, and good recovery properties.

Alternatively or in addition to vinyl trimethoxysilane and/or N-trimethoxysilylmethyl-O-methylcarbamate, 3-(2-aminoethylamino) propyltrimethoxysilane can preferably also be added to the dental molding materials according to the invention, as a functional silane. This compound represents a highly basic catalyst, on the one hand, and a crosslinking agent, on the other hand. Because of the basic properties of the amino group, this substance reacts in strongly alkaline manner, so that in the presence of water, silanols are formed with hydrolysis and release of methanol, which silanols crosslink by way of Si—O—Si bonds.

Furthermore, the two-component dental molding materials according to the invention preferably contain, particularly preferably in the catalyst component B, at least one paste forming agent h), since the latter allows the adjustment of a paste-like consistency, for example having low viscosity, medium viscosity, or high viscosity, as well as homogeneous mixing of the aqueous base and the solid reinforcing and non-reinforcing fillers b₁), b₂). Preferably, a compound selected from among the group that consists of polyethers, polyvinyl pyrrolidones, polyurethanes, polyesters, waxes, Vaseline, paraffin oils, silicon oils, glycerin, propylene glycols, polypropylene glycols, ethylene glycols, polyethylene glycols, copolymerizates of N-vinyl pyrrolidine and vinyl acetate, carboxymethylcellulose, methylcellulose, hydroxyethylcellulose, hydroxypropylcellulose, polysaccharides, glycerin, and poly(meth)acrylic acids, is used as at least one paste forming agent h). Of course, the dental molding materials according to the invention can also contain any desired combination of two or more of the aforementioned compounds. When using a free acid or a free, strong, sterically hindered base in the catalyst component B, those of the aforementioned compounds that are acid-stable or base-stable, respectively, are very particularly preferred, so that these do not react with the acid or base contained in the catalyst component B) during storage, using up hydronium or hydroxide ions, so that even after an extended storage period, the base concentration of the catalyst component B and therefore the working and curing time of the dental molding materials according to the invention remains constant.

The compounds i) that might be used as a surfactant, emulsifier, and/or stabilizer are preferably anionic surfactants, particularly preferably alkyl sulfates, alkylbenzol sulfonates, or alkylbenzol phosphates, cationic surfactants, particularly preferably tetraalkylammonium halogenides, non-ionic surfactants, particularly preferably alkyl and alkylphenyl polyalkylalkylene oxides, fatty acid alkoxylates, fatty alcohol alkyloxylates, as well as their alkyl ethers and alkyl esters, fatty acid alkylolamides, saccharose fatty acid esters, trialkylaminoxides, silicon surfactants, or fluorine surfactants, or amphoteric surfactants, particularly preferably sulfated or oxyethylated condensation products of alkenyl phenols and formaldehyde, ethylene oxide-propylene oxide block polymerizates, or modified polysiloxanes. In addition or as an alternative to this, derivatives of the aforementioned surfactants can also be used, for example those that have functional groups such as —OH, —CH═CH₂, —OCO—(CH₃)C═CH₂, as well as alkoxysilyl groups. Furthermore, other surfactants known to a person skilled in the art can be used, although these are less preferred.

Furthermore, the dental molding materials according to the invention can contain one or more active substances j) that are contained in the base component A or the catalyst component B, depending on their chemical functionality. The active substances to be used according to the invention include, in particular, astringents such as epinephrine, substances having an antibacterial and/or antifungal effect, such as hexitidine (for example 5-amino-1,3-bis(2-ethylhexyl)-5-methylhexahydropyrimidine), triclosanes (for example 2,4,4′-trichloro-2-hydroxydiphenylether) and chlorhexidine:

Possible plasticizers k) are, in particular, non-reactive polyethers, polyesters, polyurethanes, phthalates, monoesters, diesters, triesters, or esters having a higher valence, particularly acetyltributyl citrate, phthalates, and alkylsulfonic acid esters of phenol, which are added to the component A and/or the component B, depending on their chemical nature.

Compounds 1) that allow optical readability/scanning can be any substances known to a person skilled in the art for this purpose, particularly metal powders, metal pigments, metallic pigments, and titanium dioxide, which are added to the component A and/or the component B, depending on their chemical nature.

Furthermore, the dental materials according to the invention can contain usual flavors and/or fragrances m) and/or additives n) that are useful for diagnosis in one of the two or in both components, as they are described, for example, in European Patent No. EP 1 339 373, International Application No. PCT/EP00/05418, and German Patent No. DE 100 61 195.

Sodium fluoride, potassium fluoride, ammonium fluoride, fluorophosphates, and aminofluorides, such as N′-octadecyl-bimethylenediamine-N,N,N′-bis(2-ethanol)-dihydrofluoride (as described in ZM 93, No. 15, page 32 ff.) have proven to be suitable as fluoridation aids o), which can also be added to the component A and/or the component B), depending on their chemical nature.

Furthermore, the dental molding material according to the invention can contain one or more different peroxides in the component A and/or the component B, as a bleach substance p), which are preferably selected from the group that consists of alkali metal and earth alkali metal peroxides, hydrogen peroxide, as well as carbamide peroxide.

Examples of suitable desensitization agents q) are potassium salts, such as potassium nitrate, clove oil, and eugenol.

Alkoxysilanes, epoxysilanes, aminosilanes, and methacrylate silanes are particularly suitable as adhesion bond imparting agents r), for example for forming an adhesion bond between the molding material and a molding tray made of stainless steel and/or plastic.

Examples of suitable dyes s) are dye pigments in the form of Al, Ca, Ba oxides/lacquered dye, which can be added to the component A and/or the component B, depending on their chemical nature, like the ancillary substances described above, unless otherwise indicated.

Furthermore, dye indicators t) can be added to the dental molding materials according to the invention, in the component A and/or the component B, which change their color as a function of the pH, for example because of changes in pH that occur when the components A and B are mixed, or upon contact with water.

Compounds selected from the group that consists of polymer trimethyl-dihydroquinoline, diphenyl derivatives, phenothiazine, phenyl-α-naphthylamine, 4,4′-methylene-bis-2,6-di-tert.-butylphenol, butylhydroxyanisol (BHA), and methoxyphenol (hydroxyanisol), in particular, can be added to the two-component dental materials according to the invention as stabilizers and/or antioxidants u). Examples of such compounds are the products commercially available from the Ciba-Geigy company, Irganox® 1010 1076, 1035, MD 1024, Irgafos® 168, 38, Irgacor® 252 LD/252FC, 1405, 1930, 153, Tinuvin® 328, P, 384, 900, 928, 327, 1130, 400, 292, 144, 123, 622, as well as Chimassorb® 119.

Preferably, the two-component dental material according to the invention is stored in suitable primary packaging, such as tubes, jars, and particularly preferably in cartridges and tubular bags, as they are described, for example, in European Patent No. EP 0 723 807 A2, European Patent No. EP-A-0 541 972, International Application No. PCT/EP/980193, European Patent No. EP-A-0 492 412, European Patent No. EP-A-0 492 413, and European Patent No. EP 0 956 980 A1, all of which are herein incorporated by reference, and proportioned in customized amounts for later use.

Another object of the present invention is mixtures that can be obtained by means of mixing the components A and B of the two-component dental molding material according to the invention as described above. Preferably, the base component A is mixed with the catalyst component B in a ratio of 1:2 to 20:1, particularly preferably from 1:1 to 10:1, and very particularly preferably 10:1, 5:1, 4:1, 2:1, and 1:1. These mixtures are characterized by excellent wettability and an outstanding flow behavior on moist tooth and tissue substance. Despite these good hydrophilic properties, the material does not swell upon contact with aqueous media, such as water, saliva, blood, disinfection bath, or aqueous plaster paste. The good initial wettability of the mixture is important for detailed, accurate molding of the molding material in the patient's mouth during working and during the first contact with moist mouth/tooth substance, and is expressed by a low contact angle of less than 60°, preferably less than 50°, and particularly preferably less than 40°, measured using a contact angle measuring device from the Krüss company, at 20° C., with the “lying drop” measuring method. Furthermore, the cured molding material at the time plaster is cast into it (immediately or 2 hours after curing) is also characterized by a contact angle of less than 60°, preferably less than 50°, and particularly preferably less than 40°.

Accordingly, while only a few embodiments of the present invention have been shown and described, it is obvious that many changes and modifications may be made thereunto without departing from the spirit and scope of the invention. 

1. A condensation-crosslinking two-component dental molding material comprising: at least one alkoxysilyl-functional polyether a), at least one reinforcing filler b₁) having a BET surface of at least 50 m²/g or at least one non-reinforcing filler b₂) having a BET surface of less than 50 m²/g, water c), if applicable, at least one condensation catalyst d), and a hydroxylsilyl-functional polyether e).
 2. A dental molding material according to claim 1, wherein the at least one hydroxylsilyl-functional polyether e) has hydroxylsilyl structural units that are disposed exclusively terminally along a polymer backbone, and fall under the general formula SiR¹R²R³, where R¹, R² and R³, independent of one another, are hydrogen, alkyl, or hydroxy, and at least one of R¹, R² and R³ is a hydroxyl group.
 3. A dental molding material according to claim 1 wherein the at least one hydroxylsilyl-functional polyether e) has a hydroxyl group content of 0.08 to 7.0 mmol/g.
 4. A dental molding material according to claim 1, wherein individual structural units of the at least one hydroxylsilyl-functional polyether e) are disposed according to one of the following general formulas (I) and (II):

where x=1 to 6, n=1 to 6, m=0 or 1, and R¹, R² and R³, independent of one another, are hydrogen, alkyl, or hydroxyl, with at least one of R¹, R² and R³ being a hydroxyl group, and/or

where x=1 to 6, n=1 to 6, l=0 or 1, and R¹, R² and R³, independent of one another, are hydrogen, alkyl, or hydroxyl, with at least one of R¹, R² and R³ being a hydroxyl group.
 5. A dental molding material according to claim 1, wherein the at least one hydroxylsilyl-functional polyether e) has the general formula (IV)

and/or the general formula (V)


6. A dental molding material according to claim 1, wherein the material contains 10 to 80 wt.-% of at said least one polyether e).
 7. A dental molding material according to claim 1, wherein the at least one condensation catalyst d) is an organic or inorganic acid, or an organic base.
 8. A dental molding material according to claim 1, wherein the material is disposed in two components, a first component A and a second component B, and wherein the alkoxysilyl-functional polyether a) is contained in component A, and the hydroxylsilyl-functional polyether e), the water c), if applicable, as well as the catalyst d) are contained in component B, or both the alkoxysilyl-functional polyether a) and the hydroxylsilyl-functional polyether e) are contained in component A, and the water c), if applicable, as well as the catalyst d) are contained in component B.
 9. A dental molding material according to claim 1, wherein the at least one condensation catalyst d) is a metallorganic compound.
 10. A dental molding material according to claim 9, wherein the material is in two components, a first component A and a second component B, and wherein the hydroxylsilyl-functional polyether e), and the water c), if applicable, are contained in component A, and the alkoxysilyl-functional polyether a) as well as the catalyst d) are contained in component B, or both the alkoxysilyl-functional polyether a) and the hydroxylsilyl-functional polyether e) are contained in component A, and the water c), if applicable, as well as the catalyst d) are contained in component B.
 11. A mixture obtained by mixing components A and B of the two-component dental molding material according to claim 10, wherein component A is mixed with component B in a ratio of 1:2 to 20:1. 